Physical and Mechanical Properties of Resins Blends Containing a Monomethacrylate with Low-polymerization Shrinkage.

OBJECTIVES: The aim of this study was to evaluate the Knoop hardness (KH), cross-link density (CLD), water sorption (WS), water solubility (WSB), and volumetric shrinkage (VS) of experimental resins blends containing a monomethacrylate with low-polymerization shrinkage. MATERIALS AND METHODS: A blend of bisphenol glycidyl methacrylate (BisGMA) as base monomer was formulated with (Bis-GMA)/triethyleneglycol dimethacrylate (TEGDMA), Bis-GMA/isobornyl methacrylate (IBOMA), or Bis-GMA/TEGDMA/IBOMA in different concentrations (40, 50, or 60 wt%). The camphorquinone (CQ)/2-(dimethylamino) ethyl methacrylate (DMAEMA) was used as the photoinitiator system. The KH and CLD were measured at the top surface using an indenter. For WS and WSB, the volume of the samples was calculated in mm3. The samples were transferred to desiccators until a constant mass was obtained (m1) and were subsequently immersed in distilled water until no alteration in mass was detected (m2). The samples were reconditioned to constant mass in desiccators (m3). WS and WSB were determined using the equations m2 - m3/V and m1 - m3/V, respectively. VS results were calculated with the density parameters before and after curing. STATISTICAL ANALYSIS: Data were submitted to ANOVA and Tukey's test (α = 0.05). RESULTS: The resins containing IBOMA showed lower VS results. TEGDMA 40% and TEGDMA/IBOMA 20/20 wt% showed higher KH values. The IBOMA groups showed lower CLD, while TEGDMA groups had higher values of CLD. The BisGMA/TEGDMA resin presented the highest values of WS, and for WSB, all groups showed no significant differences among themselves. CONCLUSION: The monomethacrylate with low-polymerization shrinkage IBOMA used alone or in combination with TEGDMA may decrease VS, WS, and CLD values.

Improving adhesion between luting cement and zirconia-based ceramic with an alternative surface treatment.

This study evaluated the influence of an alternative surface treatment on the microshear bond strength (µsbs) of zirconia-based ceramic. Thirty-five zirconia disks were assigned to five groups according to the following treatments: Control (CO), glass and silane were not applied to the zirconia surface; G1, air blasted with 100µm glass beads + glaze + silane; G2, a gel containing 15% (by weight) glass beads applied to the ceramic surface + glaze + silane; G3, a gel containing 25% (by weight) glass beads applied to the ceramic surface + glaze + silane; and G4, a gel containing 50% (by weight) glass beads applied to the ceramic surface + glaze + silane. The specimens were built up using RelyX ARC®, according to the manufacturer's recommendations, and inserted in an elastomeric mold with an inner diameter of 0.8 mm. The µsbs test was performed using a testing machine at a crosshead speed of 0.5 mm/min. ANOVA and Tukey's test (p < 0.05) were applied to the bond strength values (in MPa). CO (15.6 ± 4.1) showed the lowest µsbs value. There were no statistical differences between the G1 (24.9 ± 7.4), G2 (24.9 ± 2.3), G3 (35.0 ± 10.3) and G4 (35.3 ± 6.0) experimental groups. Those groups submitted to surface treatments with higher concentrations of glass showed a lower frequency of adhesive failures. In conclusion, the glass application improved the interaction between the ceramic and the luting cement.

Improving adhesion between luting cement and zirconia-based ceramic with an alternative surface treatment

This study evaluated the influence of an alternative surface treatment on the microshear bond strength (μsbs) of zirconia-based ceramic. Thirty-five zirconia disks were assigned to five groups according to the following treatments: Control (CO), glass and silane were not applied to the zirconia surface; G1, air blasted with 100μm glass beads + glaze + silane; G2, a gel containing 15% (by weight) glass beads applied to the ceramic surface + glaze + silane; G3, a gel containing 25% (by weight) glass beads applied to the ceramic surface + glaze + silane; and G4, a gel containing 50% (by weight) glass beads applied to the ceramic surface + glaze + silane. The specimens were built up using RelyX ARC®, according to the manufacturer’s recommendations, and inserted in an elastomeric mold with an inner diameter of 0.8 mm. The μsbs test was performed using a testing machine at a crosshead speed of 0.5 mm/min. ANOVA and Tukey’s test (p < 0.05) were applied to the bond strength values (in MPa). CO (15.6 ± 4.1) showed the lowest μsbs value. There were no statistical differences between the G1 (24.9 ± 7.4), G2 (24.9 ± 2.3), G3 (35.0 ± 10.3) and G4 (35.3 ± 6.0) experimental groups. Those groups submitted to surface treatments with higher concentrations of glass showed a lower frequency of adhesive failures. In conclusion, the glass application improved the interaction between the ceramic and the luting cement.